Aluminum Sheet with PVC Gum Film

Model NO.: 5754

Alloy: Alloy

Sample: Free

Type: Aluminum Sheets

Shape: Flat

Trademark: Baodi

Transport Package: Wooden Pallet /Plywood Pallet /Steel Frame Pallet

Specification: SGS, ROHS

Origin: China

HS Code: 760612

Model NO.: 5754

Alloy: Alloy

Sample: Free

Type: Aluminum Sheets

Shape: Flat

Trademark: Baodi

Transport Package: Wooden Pallet /Plywood Pallet /Steel Frame Pallet

Specification: SGS, ROHS

Origin: China

HS Code: 760612

Alloy: 5754

Temper: H14, H22, H24, H18, H26, H16, H32, H34, O

Thickness(mm): 0.25-300

Width(mm): 600-2200

Length(mm): 1000-6000

Packing: Wooden/veneer pallet, wooden/veneer case

Unit Price/Payment: FOB, CIF, CFR

HS Code: 7606125900

MOQ: 2.0-2.5MT/Size

Chemical composition:
Aluminum Balance
Chromium 0.1-0.6
Copper 0.1 max
Iron 0.4max
Magnesium 2.6-3.6
Manganese 0.5
Remainder Each 0.05 max
Remainder Total 0.15 max
Silicon 0.4 max
Titanium 0.15 max
Zinc 0.2 max

Characteristic: Anti-rust material, anti-corrosion, good welding, easy to be shaped, anodized. Suitable for deep drawing.
Application: 5754 aluminum is widely used in car, ships, liquid tank, oil tank, components of car, rivet.

Brief introduction:
1. 20 years' experance in aluminum area
2. ISO 9001 Certificated
3. Have present stock for standard size
4. Small quantity is acceptable
5. 100% brand new
6. Surface: Flat, smooth, bright, no rolling mark, no black spot, no scratch
Â

Specification	Name: 5000 series Aluminum Sheet
	Alloy: 5052, 5005, 5754, 5083 etc.
	Temper: O, H12, H22, H32, H14, H24, H26, H18, H112 etc.
	Thickness: 0.2-200mm
	Width: Up to 1800mm
	Length: up to 6000mm
	Surface treatment: mill finished, PVC coated, Print marks
Feature	Machinability: It has relatively fair machinability. It is easier to machine in the hard temper than as annealed and the quality of finish is better if machined in the hard condition. Oil lubricants should be used for machining, except that very light cuts may be done dry.
	Forming: It is readily formed at room temperature. Successive cold working decreases the formability.
	Heat Treatment: It cannot be hardened by means of heat treatment. It does harden due to cold working.
	Forging: It may be forged in the temperature range of 950 FÂ down to 500 F
	Cold Working: The alloy cold works readily and may be formed by drawing or spinning. However the amount of cold work imparted by spinning makes intermediate annealing necessary.
	Annealing: Anneal at 650 FÂ and air cool.
	Hardening: Hardens only from cold working.
Application	hydraulic tubes, kitchen cabinets, small boats, home freezers, milk crates, aircraft tube, fencing, small boats, gas lines, refrigerator panels, utensils, welded pressure vessels, marine, auto aircraft cryogenics, drilling rigs, TV towers, transportation equipment, missile components etc.
Alloy	Chemical Component %â‰¤
	Si	Fe	Cu	Mn	Mg	Cr	Ni	Zn	Ti	others		Al
										single	total
5052	0.25	0.4	0.1	0.1	2.2-2.8	0.15-0.3	\	0.1	\	0.05	0.15	remainder
5005	0.3	0.7	0.2	0.2	0.5-1.1	0.1	\	0.25	\	0.05	0.15	remainder
5754	0.4	0.4	0.1	0.5	2.6-3.6	0.3	\	0.2	0.15	0.05	0.15	remainder
5083	0.4	0.4	0.1	0.4-1.0	4.0-4.9	0.05-0.25	\	0.25	0.15	0.05	0.15	remainder
Contact	Ms. Margaret			Â					Tel: 0086-15553544561

Specification	Name: 5000 series Aluminum Sheet
	Alloy: 5052, 5005, 5754, 5083 etc.
	Temper: O, H12, H22, H32, H14, H24, H26, H18, H112 etc.
	Thickness: 0.2-200mm
	Width: Up to 1800mm
	Length: up to 6000mm
	Surface treatment: mill finished, PVC coated, Print marks
Feature	Machinability: It has relatively fair machinability. It is easier to machine in the hard temper than as annealed and the quality of finish is better if machined in the hard condition. Oil lubricants should be used for machining, except that very light cuts may be done dry.
	Forming: It is readily formed at room temperature. Successive cold working decreases the formability.
	Heat Treatment: It cannot be hardened by means of heat treatment. It does harden due to cold working.
	Forging: It may be forged in the temperature range of 950 FÂ down to 500 F
	Cold Working: The alloy cold works readily and may be formed by drawing or spinning. However the amount of cold work imparted by spinning makes intermediate annealing necessary.
	Annealing: Anneal at 650 FÂ and air cool.
	Hardening: Hardens only from cold working.
Application	hydraulic tubes, kitchen cabinets, small boats, home freezers, milk crates, aircraft tube, fencing, small boats, gas lines, refrigerator panels, utensils, welded pressure vessels, marine, auto aircraft cryogenics, drilling rigs, TV towers, transportation equipment, missile components etc.
Alloy	Chemical Component %â‰¤
	Si	Fe	Cu	Mn	Mg	Cr	Ni	Zn	Ti	others		Al
										single	total
5052	0.25	0.4	0.1	0.1	2.2-2.8	0.15-0.3	\	0.1	\	0.05	0.15	remainder
5005	0.3	0.7	0.2	0.2	0.5-1.1	0.1	\	0.25	\	0.05	0.15	remainder
5754	0.4	0.4	0.1	0.5	2.6-3.6	0.3	\	0.2	0.15	0.05	0.15	remainder
5083	0.4	0.4	0.1	0.4-1.0	4.0-4.9	0.05-0.25	\	0.25	0.15	0.05	0.15	remainder
Contact	Ms. Margaret			Â					Tel: 0086-15553544561

Architecture Lighting

Classical Corrugated Lamp,Roof Tile Light,Outdoor Landscape Tree Hug Light,Outdoor Holding Lamp

Guangdong harmonglobal Lighting Co.,Ltd , https://www.harmonglobal.com